Remix each of the two components (part A and B) every time before using.

1. Mixing the components

SILBIONE RTV 4420 A&B and SILBIONE RTV 4420 QC A&B are mixed by weight in a fixed ratio given above.

The two components may be thoroughly mixed either by hand or using a low-speed electric or pneumatic mixer to minimise the introduction of air and to avoid any temperature increase.

Note: It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.


2. Degassing

The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing.

The silicone mixture expands to 3 to 4 times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.

Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio (3 to 4 times of the initial volume).

3. Polymerization

The system, as indicated in the technical data, polymerises at
 23 °C. The curing may be slowed down at lower temperature and contrary accelerated by applying heat.

Note: In general contact with certain materials can inhibit the crosslinking. See list below:

- natural rubbers vulcanised with sulphur,

- RTV elastomers catalysed with metal salts, e.g. tin-compounds,

- PVC stabilised with tin salts and additives,

- epoxy catalysed with amines,

- certain organic solvents, e.g. ketones, alcohols, ether etc.

请保存在原装密闭容器中 SILBIONE RTV 4420 QC A U1 的标准有效期是从生产日期起 6个月 请参考包装上的储存建议和失效日期。超期后,埃肯有机硅将不再保证产品符合销售规范。



SILBIONE RTV 4420 A&B and SILBIONE RTV 4420 QC A&B are a two component silicone elastomer that crosslink at room temperature by polyaddition reaction. The polymerisation can be accelerated by heat.
The silicone components are delivered as two component low viscous liquids, which once mixed and cured, transforms into a translucent, elastic and resistant material. Polymerisation occurs without formation of heat.



SILBIONE RTV 4420 A&B and SILBIONE RTV 4420 QC A&B polymerise at room temperature () even in the absence of air and moisture. The curing characteristics are independent of the thickness of the parts.

  • Fast mixing and easy processing (1 : 1) due to the low viscosity.
  • Excellent mechanical properties (especially good tear strength).


SILBIONE RTV 4420 A&B and SILBIONE RTV 4420 QC A&B are suitable for producing orthopaedic devices, e.g. damping elements.





粘度7000PairedCompISO 2555厘泊




粘度7000PairedCompISO 2555厘泊






tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13撕裂强度> 56PairedMixlb/in
hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1硬度20PairedMixASTM D 2240邵氏A
pot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6apot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6a适用期2.75PairedMixASTM C 603min
elongation_68a5ddf2-2baf-4e60-ac6f-0a8a18a758b2elongation_68a5ddf2-2baf-4e60-ac6f-0a8a18a758b2延伸率> 500PairedMixASTM D 412%





SILBIONE RTV 4420 QC B U1SILBIONE RTV 4420 QC B U1/our_offer/Product/90060084/90060083/SILBIONE-RTV-4420-QC-B-U1