Remix each of the two components (part A and B) every time before using.
1. Mixing the components
SILBIONE RTV 4420 A&B and SILBIONE RTV 4420 QC A&B are mixed by weight in a fixed ratio given above.
The two components may be thoroughly mixed either by hand or using a low-speed electric or pneumatic mixer to minimise the introduction of air and to avoid any temperature increase.
Note: It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.
2. Degassing
The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing.
The silicone mixture expands to times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio (3 to 4 times of the initial volume).
3. Polymerization
The system, as indicated in the technical data, polymerises at 23 °C. The curing may be slowed down at lower temperature and contrary accelerated by applying heat.
Note: In general contact with certain materials can inhibit the crosslinking. See list below:
- natural rubbers vulcanised with sulphur,
- RTV elastomers catalysed with metal salts, e.g. tin-compounds,
- PVC stabilised with tin salts and additives,
- epoxy catalysed with amines,
- certain organic solvents, e.g. ketones, alcohols, ether etc.


If doubts exist it’s recommendable to run a quick test with a small quantity of material in order to assess compatibility. Take duly note that cross contamination due to not well cleaned tools or devices is frequently the main causes of inhibition. The best way is to use only dedicated gear when processing polyaddition RTVs.

从生产日期开始产品SILBIONE RTV 4420 B U1保质 6个月请查看安全数据表

SILBIONE RTV 4420 B U1

SILBIONE RTV 4420 A&B and SILBIONE RTV 4420 QC A&B are a two component silicone elastomer that crosslink at room temperature by polyaddition reaction. The polymerisation can be accelerated by heat.
The silicone components are delivered as two component low viscous liquids, which once mixed and cured, transforms into a translucent, elastic and resistant material. Polymerisation occurs without formation of heat.

生物相容性

双组份室温硅橡胶

硅油

SILBIONE RTV 4420 A&B and SILBIONE RTV 4420 QC A&B polymerise at room temperature () even in the absence of air and moisture. The curing characteristics are independent of the thickness of the parts.

  • Fast mixing and easy processing (1 : 1) due to the low viscosity.
  • Excellent mechanical properties (especially good tear strength).

SILBIONE RTV 4420 A&B and SILBIONE RTV 4420 QC A&B are suitable for producing orthopaedic devices, e.g. damping elements.

亚太区;欧洲中东非洲;中南美;北美

 Characteristics_A

 

 

粘度3750PairedComp厘泊

 Characteristics_B

 

 

粘度3750PairedComp厘泊

 

 

 Table_Characteristics_A_And_B

 

 

tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13撕裂强度> 56PairedMixlb/in
hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1硬度20PairedMix邵氏A
pot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6apot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6a适用期50PairedMixmin
elongation_68a5ddf2-2baf-4e60-ac6f-0a8a18a758b2elongation_68a5ddf2-2baf-4e60-ac6f-0a8a18a758b2延伸率> 400PairedMix%

 

 

 

 

SILBIONE RTV 4420 A U1SILBIONE RTV 4420 A U1/our_offer/Product/90060081/90060082/SILBIONE-RTV-4420-A-U1

 

 

 

 

 NeedAnExpert

 

 

 CS

 

 

 SS

 

 

 PressRelease

 

 

 

 

 Brochures

 

 

Othotics & Prostheticshttps://silicones.elkem.com/ZH/Our_offer/KEC/ListInstance_Brochure_Title/OP_Flyer.pdfOthotics & Prosthetics

 TDS