Remix each of the two components (part A and B) every time before using.
1. Mixing the two components
The components A and B are mixed by weight in the above indicated ratio. The mixing can be carried out either by hand or by using a low-speed electric or pneumatic mixer to minimise the introduction of air and to avoid any temperature increase.
It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.
2. Degassing
The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing.
The silicone mixture expands to times of its initial volume and bubbles rise to the surface. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio.
3. Polymerisation
The system polymerises at . The curing may be slowed down at lower temperature or accelerated by heat.
Contact with certain materials can inhibit the crosslinking. See list below:

  • Natural rubbers vulcanised with sulphur.
  • RTV 2 silicone elastomers catalysed with metal salts, e.g. tin-compounds.
  • PVC stabilised with tin salts and additives.
  • Epoxy resins catalysed with amines.

In case of doubts, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area.

STORAGE -10°C < t < +30°C IN ITS ORIGINAL PACK STIR WELL BEFORE USEStore in a cool, dry place with adequate ventilation. Keep away from incompatible materials, open flames, and high temperatures. Store in original tightly closed container. Suitable containers: polyethylene. Steel drums coated with epoxy-resin.请查阅这个产品的物质安全数据表医疗设备一类;皮肤接触


SILBIONE RT GEL 4023 ADV A&B is a two component silicone elastomer which cures at room temperature by a polyaddition reaction. The polymerisation can be accelerated by heat.
The silicone material is delivered as two low viscous liquid components, which once mixed and cured, transform into an elastic gel. Polymerisation occurs without formation of heat.





  • Very good imitation of female breast tissue.
  • Good adhesion on PU film.
  • Prevents odour formation sometimes encountered with silicone on PU film.
  • Fast and easy processing due to low viscosity and 1:1 mixing ratio.

  • External breast prosthesis.





粘度350PairedCompISO 2555mPa.s
颜色BeigePairedCompEuropean Pharmacopea




粘度350PairedCompISO 2555mPa.s
颜色TransparentPairedCompEuropean Pharmacopea






penetration_a142c699-2b17-4f82-882a-75f6253332edpenetration_a142c699-2b17-4f82-882a-75f6253332ed针入度240PairedMixISO 21371/10mm





SILBIONE RT GEL 4023 ADV ASILBIONE RT GEL 4023 ADV A/our_offer/Product/90058416/90058417/SILBIONE-RT-GEL-4023-ADV-A






















Othotics & Prosthetics & Prosthetics