Product

 

 

1. Mixing the two components

The components A and B are mixed by weight in the above indicated ratio. The mixing can be carried out either by hand or using a low-speed electric or pneumatic mixer to minimize the introduction of air and to avoid any temperature increase.

It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.

2. Degassing

The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing.

The silicone mixture expands to 3 to 4 times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.

Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio.

3. Polymerization

The system polymerizes at 23 °C. The curing may be slowed down at lower temperature and contrary accelerated by heat.

Contact with certain materials can inhibit the crosslinking. See list below:

  • natural rubbers vulcanized with sulphur,
  • RTV 2 silicone elastomers catalyzed with metal salts, e.g. tin-compounds,
  • PVC stabilized with tin salts and additives,
  • epoxy resins catalyzed with amines,
  • certain organic solvents, e.g. ketones, alcohols, ether etc.

In case of doubts, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area.

从生产日期开始产品SILBIONE RTV 4545 B保质 6个月请查看安全数据表

SILBIONE RTV 4545 B

SILBIONE RTV 4545 A/B is a two component silicone elastomer that crosslinks at room temperature by polyaddition reaction. The polymerization can be accelerated by heat.

The silicone materials are delivered as two low viscous liquid components, which once mixed and cured, transform into an elastic and resistant material. Polymerization occurs without the evolution of heat.

生物相容性

双组份室温硅橡胶

硅油

​•Very good mechanical properties                                         

•Sterilizable                                  

•Low viscosity

•Easy processing – mixing ratio 100 : 100

•Shoe inlays

•Liners for limb prostheses 

•Prosthetic bandages

 

亚太区;欧洲中东非洲;中南美;北美

 Characteristics_A

 

 

粘度2000PairedComp厘泊

 Characteristics_B

 

 

粘度2000PairedComp厘泊

 

 

 Table_Characteristics_A_And_B

 

 

tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13撕裂强度> 45PairedMixASTM D 624lb/in
hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1硬度44.5PairedMix邵氏00
pot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6apot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6a适用期45PairedMixmin
elongation_68a5ddf2-2baf-4e60-ac6f-0a8a18a758b2elongation_68a5ddf2-2baf-4e60-ac6f-0a8a18a758b2延伸率> 600PairedMix%

 

 

 

 

SILBIONE RTV 4545 ASILBIONE RTV 4545 A/our_offer/Product/90055001/90055002/SILBIONE-RTV-4545-A

 

 

 

 

 NeedAnExpert

 

 

 CS

 

 

 SS

 

 

 PressRelease

 

 

 

 

 Brochures

 

 

 TDS