1. Mixing the two components
The components A and B are mixed by weight in the above indicated ratio. The mixing can be carried out either by hand or using a low-speed electric or pneumatic mixer to minimise the introduction of air and to avoid any temperature increase.
It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.


2. Degassing
The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing.
The silicone mixture expands to times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio.


3. Polymerisation
The system polymerises at . The curing may be slowed down at lower temperature and contrary accelerated by heat.
Contact with certain materials can inhibit the crosslinking. See list below:

  • natural rubbers vulcanised with sulphur,
  • RTV 2 silicone elastomers catalysed with metal salts, e.g. tin-compounds,
  • PVC stabilised with tin salts and additives,
  • epoxy resins catalysed with amines,
  • certain organic solvents, e.g. ketones, alcohols, ether etc.


In case of doubts, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area.

 

SILBIONE RT GEL 4122 A 储存温度要介于 -10 °C/ 14 °F 和 30 °C/ 86 °F 之间,从生产日期开始产品保质 6 个月请查看安全数据表医疗设备一类;皮肤接触

SILBIONE RT GEL 4122 A

SILBIONE RT GEL 4021 QC A&B and SILBIONE RT GEL 4122 A&B are two component silicone elastomers that crosslink at room temperature by polyaddition reaction. The polymerisation can be accelerated by heat.
The silicone materials are delivered as two low viscous liquid components, which once mixed and cured, transform into an elastic and resistant gel. Polymerisation occurs without formation of heat.

生物相容性

双组份室温硅橡胶

硅油

医疗设备一类;皮肤接触

 

  • Very good imitation of female tissue
  • Good adhesion on PU film
  • Fast curing at elevated temperature

 

 

  • External breast prosthesis
  • Bra pads

 

亚太区;欧洲中东非洲;中南美;北美

 Characteristics_A

 

 

粘度< 200PairedCompISO 2555mPa.s
颜色TransparentPairedCompEuropean Pharmacopea

 Characteristics_B

 

 

粘度< 2000PairedCompISO 2555mPa.s
颜色PinkPairedCompEuropean Pharmacopea

 

 

 Table_Characteristics_A_And_B

 

 

penetration_a142c699-2b17-4f82-882a-75f6253332edpenetration_a142c699-2b17-4f82-882a-75f6253332ed针入度210PairedMixISO 21371/10mm
pot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6apot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6a适用期15PairedMixmin

 

 

 

 

SILBIONE RT GEL 4122 BSILBIONE RT GEL 4122 B/our_offer/Product/90053427/90053426/SILBIONE-RT-GEL-4122-B

 

 

 

 

 NeedAnExpert

 

 

 CS

 

 

 SS

 

 

 PressRelease

 

 

 

 

 Brochures

 

 

Othotics & Prostheticshttps://silicones.elkem.com/ZH/Our_offer/KEC/ListInstance_Brochure_Title/OP_Flyer.pdfOthotics & Prosthetics

 TDS