Product

 

 

Remix each of the two components (parts A and B) every time before using.
1. Mixing of the two components
Add 100 parts of BLUESIL RTV to 10 parts of BLUESIL RTV 3460 B.
The two components may be intimately mixed either by hand or using a low-speed electric or pneumatic mixer to minimize the introduction of air into the mixture.
2. Degassing
After mixing BLUESIL RTV 3460 A&B, it is recommended to eliminate entrapped air. If the processing is done with the help of a mixing machine both parts are degassed before mixing.
The BLUESIL RTV 3460 A&B is degassed under a vacuum of 30 to 50 mbar. Under vacuum, the product expands 3 times its initial volume and forms bubbles on its surface. These bubbles will disappear gradually and the mixture will sink back down to its initial volume within 5 minutes. Release the vacuum and repeat the operation a few minutes later.
Remark: release the vacuum several times imes the degassing. For easier degassing only fill a recipient to 1/3 of its height.


3. Cross linking
The best curing conditions are at . The use of products at higher temperatures will reduce the pot life and increase the setting rate. As opposed to this, lower temperatures will increase the pot life and decrease the setting time. It is recommended not to use the product at temperatures below 20?C under these conditions, the final product performance levels will be difficult to achieve.
At 23?C, the moulds can be demoulded after 16 hours. In order to achieve the best possible performance levels from the moulds it is preferable to wait for 24 hours before using them.
Room temperature curing assures the lowest possible shrinkage, if accelerated cure is desired, mild heat should be preferred. To minimize shrinkage cure the elastomer at maximum temperature of for 3-4 hours, higher temperatures will cause higher shrinkage.
Conversely at lower temperature polymerization is much slower, at 36 hours may be necessary to complete cross-linking.
Be aware that contact with certain materials can inhibit the curing of this RTV:

  • Natural rubbers vulcanized with sulphur
  • Polycondensation RTV catalysed with metal salts
  • PVC stabilizing agents
  • Amine cured epoxies
  • Sulphur containing clays.

If doubts exist it’s recommendable to run a quick test with a small quantity of material in order to assess compatibility. Take duly note that cross contamination due to not well cleaned tools or devices is frequently the main cause of inhibition. The best way is to use only dedicated gear when processing polyaddition RTVs.

STORAGE t < +40°C IN ITS ORIGINAL PACKStore in a cool, dry place with adequate ventilation. Keep away from incompatible materials, open flames, and high temperatures. Store in tightly closed original container. equipped with a degassing device. Suitable containers: polyethylene. Steel drums coated with epoxy-resin.请查阅这个产品的物质安全数据表

BLUESIL RTV 3460 B BLACK

The BLUESIL RTV 3460 A&B – is a two component silicone elastomer which cures at room temperature by a polyaddition reaction (10:1 ratio). It is designed as a high durometer rubber offering high mechanical strength and a long mold life.

离型

双组份室温硅橡胶

硅油

  • Outstanding mechanical resistance at high durometer
  • Resistance to common casting resins
  • Low density
  • Excellent details reproduction

This product is specifically formulated for use with casting materials and urethane foams for architectural, prototyping and furniture molding applications. BLUESIL RTV 3460 A&B is also used in high pressure applications (PU Foam, RIM).

亚太区;欧洲中东非洲;中南美;北美

 Characteristics_A

 

 

 Characteristics_B

 

 

 

 

 Table_Characteristics_A_And_B

 

 

 

 

 

 

BLUESIL RTV 3460 ABLUESIL RTV 3460 A/our_offer/Product/90038788/90038789/BLUESIL-RTV-3460-A

 

 

 

 

 NeedAnExpert

 

 

 CS

 

 

 SS

 

 

 PressRelease

 

 

 

 

 Brochures

 

 

 TDS