1. Mixing the two components

The components A and B are mixed by weight in the above indicated ratio. The mixing

can be carried out either by hand or using a low-speed electric or pneumatic mixer to

minimise the introduction of air and to avoid any temperature increase.

It is also possible to use a special mixing and dispensing machine for the two silicone

components. Further information is available upon request.

2. Degassing

The mixture should be degassed preferably at 30 to 50 mbar to eliminate any

entrapped air. If a dispensing machine is used, the two components are degassed

separately prior to mixing.

The silicone mixture expands to 3 to 4 times of its initial volume and bubbles rise to

the surface. The bubbles progressively disappear and the mixture returns to its initial

volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then

flash the vacuum. The silicone is ready for pouring, either by gravity or under low


Note: Flashing the vacuum once or twice accelerates the degassing. It is

recommended to use a container with a high diameter / height ratio.

3. Polymerisation

The system polymerises at 23°C. The curing may be slowed down at lower

temperature and contrary accelerated by heat.

Contact with certain materials can inhibit the crosslinking. See list below:

· natural rubbers vulcanised with sulphur

· RTV 2 silicone elastomers catalysed with metal salts, e.g. tin-compounds

· PVC stabilised with tin salts and additives

· epoxy resins catalysed with amines

In case of doubts, it is recommended to test the substrate by applying a small quantity

of the mixed silicone on a restricted area.

SILBIONE RTV 4410 1/1 A 储存温度要介于 -10 °C/ 14 °F 和 30 °C/ 86 °F 之间,从生产日期开始产品保质 6 个月请查看安全数据表医疗设备一类;皮肤接触


The SILBIONE RTV 4410 1:1, 4410 QC Trans, 4411 A & B are two component

silicone elastomers that crosslink at room temperature by polyaddition reaction. The

polymerisation can be accelerated by heat.

The silicone materials are delivered as two low viscous liquid components, which once

mixed and cured, transform into an elastic and resistant material. Polymerisation

occurs without formation of heat.





  • Very good mechanical properties
  • Suitable for adhesive gel coatings (see Bluestar Adhesive Gels range)
  • Sterilisable
  • Low viscosity
  • Easy processing - mixing ratio 1 : 1
  • Shoe inlays
  • Liners for limb prostheses
  • Prosthetic bandages





颜色TranslucentPairedCompEuropean Pharmacopea




颜色TranslucentPairedCompEuropean Pharmacopea






tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13撕裂强度> 10PairedMixDIN 53515N/mm
elongation_68a5ddf2-2baf-4e60-ac6f-0a8a18a758b2elongation_68a5ddf2-2baf-4e60-ac6f-0a8a18a758b2延伸率> 530PairedMixDIN 53504%





SILBIONE RTV 4410 1/1 BSILBIONE RTV 4410 1/1 B/our_offer/Product/90038522/90038521/SILBIONE-RTV-4410-1-1-B






















Othotics & Prosthetics & Prosthetics