  • Mixing the two components

The components A and B are mixed by weight in the above indicated ratio. The mixing can be carried out either by hand or using a low-speed electric or pneumatic mixer to minimise the introduction of air and to avoid any temperature increase.
It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.
  • Degassing

The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing.
The silicone mixture expands to times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio.
  • Polymerisation

The system polymerises at . The curing may be slowed down at lower temperature and contrary accelerated by heat.
Contact with certain materials can inhibit the crosslinking. See list below:
  • natural rubbers vulcanised with sulphur,
  • RTV 2 silicone elastomers catalysed with metal salts, e.g. tin-compounds,
  • PVC stabilised with tin salts and additives,
  • epoxy resins catalysed with amines.

In case of doubts, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area.

BLUESIL RTV 3040 HARD B 1/1 储存温度要介于 -10 °C/ 14 °F 和 30 °C/ 86 °F 之间,从生产日期开始产品保质 12 个月请查看安全数据表

BLUESIL RTV 3040 HARD B 1/1

BLUESIL RTV 3040 HARD A&B 1:1 is a two component silicone elastomer that crosslinks at room temperature by polyaddition reaction. The polymerisation can be accelerated by heat (max. ).
The silicone components are delivered as two viscous liquids, which once mixed and cured, transform into a transparent, elastic and resistant material. Polymerisation occurs without production of heat.

光学透明性;离型

双组份室温硅橡胶

硅油

  • accurate reproduction of details
  • very good transparency
  • exceptional mechanical properties
  • free matching within product range

  • Reproduction of 3D objects in polyurethane, waxes, foams, epoxy, polyester, etc.

欧洲中东非洲;中南美

 Characteristics_A

 

 

粘度56000PairedCompBSI HL 019mPa.s
颜色TransparentPairedComp

 Characteristics_B

 

 

粘度56000PairedCompBSI HL 019mPa.s
颜色TransparentPairedComp

 

 

 Table_Characteristics_A_And_B

 

 

hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1硬度37PairedMixDIN 53505邵氏A
pot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6apot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6a适用期60PairedMixBSI HL 016min
tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13撕裂强度22PairedMixDIN 53515N/mm

 

 

 

 

BLUESIL RTV 3040 HARD A 1/1BLUESIL RTV 3040 HARD A 1/1/our_offer/Product/90038039/90038041/BLUESIL-RTV-3040-HARD-A-1-1

 

 

 

 

 NeedAnExpert

 

 

 

 

 CS

 

 

 SS

 

 

 PressRelease

 

 

 

 

 Brochures

 

 

 TDS