It is advised to remix both base and catalyst before mixing them together.
1. Mixing of the two components
To 100 parts of BLUESIL RTV 3322 add 5 parts of Catalyst 24H or 6H.
The two components are thoroughly mixed either using an electrical or pneumatic mixer on a low speed setting so as to limit the inclusion of air in the mixture as well as temperature rise.


2. Degassing
After mixing base and catalyst, it is recommended to degas to eliminate entrapped air.
If the processing is done with the help of a machine both parts are degassed before mixing.
The BLUESIL RTV 3322 is degassed under vacuum pressure of 30 to 50 mbar.
Under vacuum pressure, the product will expand 3 at 4 times its initial volume and forms bubble on its surface.
These bubbles will disappear gradually and the mixture will sink back down to its initial volume within 5 to 10 minutes. Release the vacuum and repeat the operation a few minutes later.
Remark: release the vacuum several times improves the degassing. For easier degassing only fill a recipient to 1/3 of its height.


3. Cross linking
The best curing conditions are at 23 °C and 50 % relative humidity. The use of products at higher temperatures and/or relative humidity levels will reduce the pot life and increase the setting rate. As opposed to this, lower temperatures and relative humidity levels will increase the pot life and decrease the setting time. It is recommended not to use the product at temperatures below 20 °C; under these conditions, the final product performance levels will be difficult to achieve.
At 23 °C and 50 % relative humidity, the membranes can be de-moulded after 16 to 24 hours. In order to achieve the best possible performance levels from the membranes, it is preferable to wait for 24 hours before using them. The definitive properties will be acquired after 3 days.

BLUESIL RTV 3322 储存温度要低于 40 °C/ 104 °F ,从生产日期开始产品保质 12个月请查看安全数据表

BLUESIL RTV 3322

BLUESIL RTV 3322 is a silicone elastomer which, after the addition of catalysts BLUESIL 24H or BLUESIL 6H, cures at room temperature and leads to a flexible and elastic material.

离型

双组份室温硅橡胶

硅油

 

  • Good fluidity.
  • Very good mechanical properties, in particular tear strength.
  • Very good flexibility and its low modulus facilitate mould release.
  • Odourless catalysts.

 

Moulds for the production of parts made of different materials, such as plaster, wax, acrylic resin, polyester resin, epoxy resin, as well as silicone elastomers, with following application examples:

  • Decoration items: cornices, , ornaments, statues,  
  • Figurines: toys, candles, statues, giftware,
  • Furnishing: furniture and decorative parts,
  • Construction: decorative items, pavement, paving stone, columns, 
  • Artistic foundries: molds for the lost wax casting technique. 

 

亚太区;欧洲中东非洲;中南美

 Characteristics_A

 

 

颜色BeigePairedComp
粘度30000PairedCompmPa.s

 Characteristics_B

 

 

颜色Yellow / ColourlessPairedComp
外观LiquidPairedComp

 

 

 Table_Characteristics_A_And_B

 

 

pot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6apot-life_0d649a54-7503-4c7c-a047-9d0c4b3e9f6a适用期120PairedMixmin
hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1硬度22PairedMix邵氏A
tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13tear-strength_a14604f3-602f-4240-a9bf-15d90bbfbd13撕裂强度15PairedMixKN/m

 

 

 

 

BLUESIL CATA 24HBLUESIL CATA 24H/our_offer/Product/90039341/90000419/BLUESIL-CATA-24H

 

 

 

 

 NeedAnExpert

 

 

 

 

 CS

 

 

 SS

 

 

 PressRelease

 

 

 

 

 Brochures

 

 

 TDS