To determine the exact concentration to be used in each particular case, it is advisable to make the first tests with an emulsion obtained by diluting one part of BLUESIL EMUL 35B with 30 parts of water. Simply add the necessary quantity of water to the emulsion and stir.
If mould release or the surface finish of the moulded article are not satisfactory, the concentration of BLUESIL EMUL 35B should be increased gradually. Simply add BLUESIL EMUL 35B until satisfactory results are obtained. Stirring is important during addition.
If the concentration of 1 : 30 is satisfactory, add water gradually, stirring each time, to find the minimum concentration which still provides good mould release.
Application by a spray gun is recommended. When set to give a very fine spray, a thin, even film is obtained.
The emulsion can also be applied with a brush or a pad, but this is less economical.
One application is generally sufficient for several mould releases, but many users prefer to apply a more dilute emulsion before each moulding.
The emulsion should be applied:
- On perfectly clean, grease-free moulds. Traces of moulded material or alkaline pickling solutions would prevent the silicone from spreading perfectly over the surface of the mould and would therefore cause surface defects.
- To moulds heated to at least 110-120 °C, to ensure instantaneous evaporation of the water, which must be eliminated before moulding.
- Diluted - the use of undiluted or insufficiently diluted BLUESIL EMUL 35B would cause faulty moulding by impairing material solidification, without improving mould release.
|PROTECT FROM FREEZING||Avoid discharge into drains, water courses or onto the ground. Store in a cool, dry place with adequate ventilation. Keep away from incompatible materials, open flames, and high temperatures. Avoid contact with oxidizing agents. Suitable containers: Steel drums coated with epoxy-resin.||请查阅这个产品的物质安全数据表||欧盟《电气、电子设备中限制使用某些有害物质指令》|
BLUESIL EMUL 35B
BLUESIL EMUL 35B is an oil-in-water emulsion containing 35 % silicone oil, which is diluted for use, generally in a proportion of one part of BLUESIL EMUL 35B to 20 to 200 parts of water.
Its characteristics are as follows:
- Practically no tendency to cream, neither during storage nor in use.
- Perfect stability in contact with hard water or zinc (i.e. in galvanized metal containers).
- Excellent heat stability after dilution.
- Very good wetting power.
BLUESIL EMUL 35B offers the following advantages:
It does not decompose at normal moulding temperatures, and therefore leaves no sooty or other deposits on the moulds or moulded articles.
It imparts an attractive finish to the moulded articles and keeps the moulds perfectly clean.
Hydrophobic and chemically inert:
BLUESIL EMUL 35B is hydrophobic and chemically inert. It thus protects the surface of the mould against corrosion during and after moulding.
Immiscibility with the moulding material:
It is immiscible with nearly all types of natural and synthetic rubbes and plastics. It wets the surface, forming a continuous film which prevents the material from adhering even to the sides of the mould.
This property enables BLUESIL EMUL 35B to improve the ageing characteristics of certain rubber articles, such as bags, mats, etc.
BLUESIL EMUL 35B was specially formulated to lubricate moulds so as to make mould-release easier in the rubber and plastics industries.
- Removing tyres from moulds
Use one part of BLUESIL EMUL 35B for 30 to 125 parts of water, depending on the moulding mixture, the tyre tread and curing time.
Spray onto the hot mould before each moulding step. Avoid applying too much emulsion.
- Lubricating curing bags
Use one part of BLUESIL EMUL 35B for 35 parts of water.
Some manufacturers add one part of glycerine to one part of BLUESIL EMUL 35B before dilution.
Apply by dipping or spraying.
- Removing rubber soles, heels and mats from moulds
Dilute one part of BLUESIL EMUL 35B with 30 to 150 parts of water. Spray on to the mould.
In the manufacture of mats, the use of BLUESIL EMUL 35B reduces rejects due to tearing and, by making mould-release quicker, reduces the total curing cycle time.
- Removing miscellaneous rubber articles from moulds
Use one part of BLUESIL EMUL 35B for 30 to 200 parts of water, depending on the composition of the moulding mixture, the complexity of the mould and curing time.
Spray on to the mould.
Substituting BLUESIL EMUL 35B for organic lubricants considerably reduces the frequency with which moulds need cleaning.
- Removing plastics from moulds
As above, use one part of BLUESIL EMUL 35B for 30 to 200 parts of water, as required, and spray on.
BLUESIL EMUL 35B is perfectly suitable for mould release of phenolic resins, urea-formaldehyde and melamine-formaldehyde resins, acrylic resins, and polyethylene and polyvinyl chloride sheets.
When sheets are being grained, it prevents them from sticking to the rollers.
When the moulding temperature is below , it is more convenient to use BLUESIL FLD 47V350 instead of BLUESIL EMUL 35B. It should be dispersed in a concentration of 0.5 to 2 % in a solvent such as white spirit, cyclohexane, pentane, xylene or BLUESIL FLD 41V 0.65.
- Manufacturing nylon stockings
Applying BLUESIL EMUL 35B to the aluminium forms used for making nylon stockings makes it easier to remove the stockings and reduces wast due to snagged threads.
Use one part of BLUESIL EMUL 35B for 5 to 10 parts of water. Preferably apply with a cloth to the hot form.
- Manufacturing rubber-sheathed wires and cables
In cable-manufacturing, BLUESIL EMUL 35B is used to lubricate the surface of rubber-sheated wires and cables to prevent the risk of sticking, thus making subsequent operations easier.
It is generally applied continuously by passing the wire through a very dilute bath of BLUESIL EMUL 35B.