Remix each of the 2 components (base and catalyst) every time before using.
1. Mixing of the two components
To 100 parts of BLUESIL RTV 3221 add 5 parts by weight of the selected catalyst. The two components are thoroughly mixed either using an electrical or pneumatic mixer, on a low speed setting so as to limit the inclusion of air in the mixture as well as the temperature rise.

2. Degassing
After mixing base and catalyst, it is recommended to eliminate entrapped air. If the processing is done with the help of a machine both parts are degassed before mixing.
The BLUESIL RTV 3221 is degassed under a vacuum of 30 to 50 mbar.
Under vacuum pressure, the product will expand 3 at 4 times its initial volume and forms bubbles on its surface.
These bubbles will disappear gradually and the mixture will sink back down to its initial volume within 5 minutes. Release the vacuum and repeat the operation a few minutes later.
Remark: release the vacuum several times improves the degassing. For easier degassing only fill a recipient to 1/3 of its height.

3. Cross linking
The best curing conditions are at 23°C and 50 % relative humidity. The use of products at higher temperatures and / or relative humidity levels will reduce the pot life and increase the setting rate.
As opposed to this, lower temperatures and relative humidity levels will increase the pot life and decrease the setting time. It is recommended not to use the product at temperatures below 20°C under these conditions, the final product performance levels will be difficult to achieve.
At 23°C and 50 % relative humidity, the moulds can be demoulded after 6 hours for BLUESIL CATA 6H and 24 hours for BLUESIL CATA 24H. In order to achieve the best possible performance levels from the moulds, it is preferable to wait for 24 hours before using them. The definitive properties will be acquired after 3 days.

BLUESIL RTV 3221 储存温度要低于 40 °C/ 104 °F ,从生产日期开始产品保质 18个月请查看安全数据表

BLUESIL RTV 3221

BLUESIL RTV 3221 is a silicone elastomer which, after the addition of catalyst, cures at room temperature and leads to flexible and elastic material.

双组份室温硅橡胶

硅油

 

  • Good fluidity.
  • Excellent flexibility and its low modulus facilitate mould release.
  • Range of catalysts allows the BLUESIL RTV 3221 to fulfil requirements for various applications:
  • BLUESIL CATA 24H: standard kinetics (24 hours demould)
  • BLUESIL CATA 6H: fast kinetics (6 hours demould)
These catalysts have the advantage of being odourless.

 

Production of high-flexibility moulds used in the art and decoration field:

  • Mouldings for single reproduction or for those limited to only a few examples: theatrical, movies industry and television special effects and statuary arts.
  • Wax mouldings for artistic foundry work and fancy jewellery.
  • Repeated mouldings: production of figurines.
  • Mouldings in the craft and "Do it yourself" fields
  • Building trade: pre-production of decorative items.

 

亚太区;欧洲中东非洲;中南美

 Characteristics_A

 

 

粘度15000PairedCompRH 0174mPa.s
颜色BeigePairedComp

 Characteristics_B

 

 

颜色Yellow / ColourlessPairedComp
外观LiquidPairedComp

 

 

 Table_Characteristics_A_And_B

 

 

hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1硬度18PairedMixRH 0149邵氏A

 

 

 

 

BLUESIL CATA 24HBLUESIL CATA 24H/our_offer/Product/90039341/90000419/BLUESIL-CATA-24H

 

 

 

 

 NeedAnExpert

 

 

 CS

 

 

 SS

 

 

 PressRelease

 

 

 

 

 Brochures

 

 

 TDS