Remix each of the two components (base and catalyst) every time before using.

1. Mixing of the two components
To 100 parts of BLUESIL RTV 3220 LV add 5 parts by weight of BLUESIL CATA 2H. The two components are thoroughly mixed either using an electrical or pneumatic mixer, on a low speed setting so as to limit the inclusion of air in the mixture as well as the temperature rise.


2. Degassing
After mixing BLUESIL RTV 3220 LV and BLUESIL CATA 2H, it is recommended to eliminate entrapped air.
The catalysed BLUESIL RTV 3220 LV is degassed under a vacuum of 30 to 50 mbar. Under vacuum, the product expands 3 to 4 times its initial volume and forms bubbles on its surface. These bubbles will disappear gradually and the mixture will sink back down to its initial volume within few minutes. Release the vacuum and repeat the operation a few minutes later.
Remark: release the vacuum several times imes the degassing. For easier degassing only fill a recipient to 1/3 of its height


3. Cross linking
The best curing conditions are at and 50% relative humidity. The use of the products at higher temperatures and / or relative humidity levels will reduce the pot life and increase the setting rate. As opposed to this, lower temperatures and relative humidity levels will increase the pot life and decrease the setting rate.
It is suggested not to place the catalysed product, during or after crosslinking, to temperatures above .
At 23°C and 50% relative humidity, the moulds can be demoulded after 3 hours. In order to achieve the best possible performance levels from the moulds, it is preferable to wait for 24 hours before using them. The definitive properties will be acquired after 3 days.

4. How to use
Apply BLUESIL RTV 3220 LV mixed with CATA 2H directly on the model by casting, trying to avoid bubbles and voids.
Models can be made of several materials, stones, concrete, metal, etc. Even though silicone is naturally no-adhering to most materials is always recommendable to prepare the model to avoid any risk of the silicone sticking and so damaging the model. Remove dust and apply a pore filler like soapy water, waxes diluted in xylene, etc.
Part used drums should be resealed between each use.

BLUESIL RTV 3220 LV 储存温度要低于 40 °C/ 104 °F ,从生产日期开始产品保质 12个月请查看安全数据表

BLUESIL RTV 3220 LV

BLUESIL RTV 3220 LV is a silicone elastomer which cures at room temperature by a polycondensation reaction.
After the addition of catalyst BLUESIL CATA 2H, it cures at room temperature and leads to flexible and elastic material.

双组份室温硅橡胶

硅油

  • Easy processing.
  • Low linear shrinkage.
  • Excellent reproduction of details.

Production of high-flexibility moulds used for soles shoes or technical products.

亚太区;欧洲中东非洲;中南美

 Characteristics_A

 

 

粘度7000PairedCompRH 0174mPa.s
颜色BeigePairedComp

 Characteristics_B

 

 

颜色RedMonocomp
外观LiquidMonocomp

 

 

 Table_Characteristics_A_And_B

 

 

hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1hardness_cd523e03-72a3-4261-93f9-36f7bbeeafb1硬度20PairedMixRH 0149邵氏A

 

 

 

 

BLUESIL CATA 2H REDBLUESIL CATA 2H RED/our_offer/Product/90054883/90000419/BLUESIL-CATA-2H-RED

 

 

 

 

 NeedAnExpert

 

 

 CS

 

 

 SS

 

 

 PressRelease

 

 

 

 

 Brochures

 

 

 TDS