1. Mixing the two components
The components A and B are mixed by weight in the above indicated ratio. The mixing can be carried out either by hand or using a low-speed electric or pneumatic mixer to minimize the introduction of air and to avoid any temperature increase. It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.
The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing. The silicone mixture expands to 3 to 4 times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio.
The system polymerizes at 23°C. The curing may be slowed down by lowering the temperature and accelerated by adding heat.
Contact with certain materials can inhibit the crosslinking. See list below:
• natural rubbers vulcanized with sulphur,
• RTV 2 silicone elastomers catalyzed with metal salts, e.g. tin-compounds,
• PVC stabilized with tin salts and additives,
• epoxy resins catalyzed with amines,
• certain organic solvents, e.g. ketones, alcohols, ether etc.
In case of doubts, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area.
|BLUESIL RTV 3611 QC B may be stored at a temperature below 40°C / 104°F for up to 6 months from its date of manufacturing.||Please consult the Safety Data Sheet of this product.|
BLUESIL RTV 3611 QC B
BLUESIL RTV 3611 QC A&B is a two component, 10 Shore A durometer, room temperature, quick cure silicone elastomer designed for use in special effects and moldmaking applications, especially where flexibility and repetitive motion is required. It's superior physical properties and softness also allows use in non-skin contact cushioning applications.
2 Part RTV
•Translucent – can be pigmented
•Easy to use
•Excellent combination of softness and mechanical strength
•Animatronics; special effect skins
•Props for the film industry
•Theme park props and reproduction molds