1. Mixing the two components
The components A and B are mixed by weight in the above indicated ratio. The mixing can be carried out either by hand or using a low-speed electric or pneumatic mixer to minimise the introduction of air and to avoid any temperature increase.
It is also possible to use a special mixing and dispensing machine for the two silicone components. Further information is available upon request.

2. Degassing
The mixture should be degassed preferably at 30 to 50 mbar to eliminate any entrapped air. If a dispensing machine is used, the two components are degassed separately prior to mixing.
The silicone mixture expands to times of its initial volume and bubbles rise to the surface. The bubbles progressively disappear and the mixture returns to its initial volume after 5 to 10 minutes. Wait a few minutes to complete the degassing and then flash the vacuum. The silicone is ready for pouring, either by gravity or under low pressure.
Note: Flashing the vacuum once or twice accelerates the degassing. It is recommended to use a container with a high diameter / height ratio.

3. Polymerisation
The system polymerises at . The curing may be slowed down at lower temperature and contrary accelerated by heat.
Contact with certain materials can inhibit the crosslinking. See list below:

  • Natural rubbers vulcanised with sulphur,
  • RTV 2 silicone elastomers catalysed with metal salts, e.g. tin-compounds,
  • PVC stabilised with tin salts and additives,
  • epoxy resins catalysed with amines,

In case of doubts, it is recommended to test the substrate by applying a small quantity of the mixed silicone on a restricted area.


SILBIONE HC2 2031 B may be stored at a temperature between -10 °C/ 14 °F and 30 °C/ 86 °F for up to 12 months from its date of manufacturing.Please consult the Safety Data Sheet of this product.Healthcare Class I;Skin Contact


SILBIONE HC2 2031 A&B is a two component silicone elastomer that crosslinks at room temperature by polyaddition reaction. The polymerisation can be accelerated by heat.
The silicone material is delivered as two low viscous liquid components, which once mixed and cured, transform into an elastic and resistant gel. Polymerisation occurs without formation of heat.

Adhesion;Bio-compatibility;Coating;Fabric Coating

2 Part RTV


Healthcare Class I;Skin Contact


  • Very good adhesion on dry skin.
  • No adhesion on moist wounds.
  • Proven biocompatibility.
  • No free oil.



  • Medical (< 30 days implantable).
  • Adhesive wound dressings.
  • Adhesive sheets in medical applications.


Asia Pacific;Europe Middle East Africa;Central and South America;North America




ColorTransparentPairedCompASTM D 412
Viscosity47500PairedCompNF T 76102mPa.s




ColorTransparentPairedCompASTM D 412
Viscosity52500PairedCompNF T 76102mPa.s






penetration_a142c699-2b17-4f82-882a-75f6253332edpenetration_a142c699-2b17-4f82-882a-75f6253332edPenetration169PairedMixISO 21371/10mm





SILBIONE HC2 2031 ASILBIONE HC2 2031 A/our_offer/Product/90059162/90059163/SILBIONE-HC2-2031-A













Healthcare Silicone: Wound Care Silicone: Wound Care