Parts A and B components of SILBIONE HCRA 4170 A/B HC are designed to be mixed in equal parts by weight or volume using standard rubber processing techniques such as two roll milling. For optimum results, freshen both parts separately on the two roll mill before mixing them. Do not allow the material temperature to exceed 30°C during the milling. The mixed material should be used within two hours to prevent structuring and premature crosslinking. Molding is typically 10 minutes at 120°C or 3 minutes at 165°C.

SILBIONE HCRA 4170 HC KIT may be stored for up to 12 months from its date of manufacturing.Please consult the Safety Data Sheet of this product.


SILBIONE® HCRA 4170 A/B HC is a two-part, addition-cure, platinum catalyzed silicone elastomer designed for use in processes where high strength molded parts or extruded profiles are desired. It is formulated for rapid cure in transfer and compression molds and in short-dwell vulcanizing ovens for extrusion processes. SILBIONE ® HCRA 4170 A/B HC is formulated to meet the requirements of USP Class VI.


Custom Compound HCR

• No volatile cure by-products

• Optional post cure

• Non-tacky surface

• Non-blooming

• No peroxide residue

 • Molded or extruded medical parts for <30 day implantation

• Healthcare applications: stoppers, plungers, seals, needle entry ports, tubing

Asia Pacific;Europe Middle East Africa;Central and South America;North America




Specific Gravity1.17MonocompISO 1183
Elongation> 500MonocompASTM D 412%