Parts A and B components of SILBIONE HCRA 4165 A/B HC are designed to be mixed in equal parts by weight or volume using standard rubber processing techniques such as two roll milling. For optimum results, freshen both parts separately on the two roll mill before mixing them. Do not allow the material temperature to exceed 30°C during the milling. The mixed material should be used within two hours to prevent structuring and premature crosslinking. Molding is typically 10 minutes at 120°C or 3 minutes at 165°C.

Please consult the Safety Data Sheet of this product.


SILBIONE HCRA 4165 A/B HC is a two-part, addition-cure, platinum catalyzed silicone elastomer designed for use in processes where high strength molded parts or extruded profiles are desired. It is formulated for rapid cure in transfer and compression molds and in short-dwell vulcanizing ovens for extrusion processes. SILBIONE HCRA 4165 A/B HC meets USP Class VI requirements and can be used in short term (under 30 days) implant materials.


Custom Compound HCR


•No volatile cure by-products

•Optional post cure

•Non-tacky surface


•No peroxide residue

• Molded or extruded medical parts for <30 day implantation

• Healthcare applications: stoppers, plungers, seals, needle entry ports, tubing

Asia Pacific;Europe Middle East Africa;Central and South America;North America

For information about Storage and Shelf Life for this product, please download the Technical Data Sheet.




Specific Gravity1.16MonocompASTM D 792
Elongation> 600MonocompASTM D 412%