is a white, two component, addition cure, heat curing silicone compound. It
is designed as a protective coating for light sensitive electronic circuits
and devices. BLUESIL ™ V-204 is unique in that it
is semi-thixotropic for blob-top coating, yet when stirred;
it becomes flowable for conformal coating.
• Protective coating for opto-couplers and other light
1. Mix Part A and Part B components according to recommended weight ratios. If power equipment is to be used, it is generally recommended to keep mixing speed at or below 350 rpm to prevent heat buildup, which can cause loss of working time and premature curing of the rubber. It is recommended that the container be filled to not more than 1/3 the container height to allow sufficient room for expansion during the deaeration procedure.
2. For these products requiring deaeration, place mixed material in a vacuum chamber and exert 29 inches Vacuum on the material. Some products will require that the vacuum be interrupted or "bumped" several times before the material crests and falls by itself. After the material has receded, keep the mixed material under full vacuum for a minimum of 15 minutes. Bleed air slowly into the chamber until atmospheric equilibrium is reached. Remove mixed and vacuumed material from the chamber. The material is now ready for pouring.
3. Some Bluestar Silicones Aerospace and Industrial products have a very long mixed pot life. Storing the mixture in a tightly sealed container at 0°F (-18°C) may extend the pot life even longer. Care should be taken when using this method to prevent moisture from condensing on the inside of cold containers and contaminating