Some fillers may settle during transport and storage. To ensure a uniform mix, the components should be thoroughly stirred prior to use.
In case of hand mixing, degas the mix under vacuum 3-5 kPa before processing the product. Use preferably static mixing equipment to prevent bubbles and voids formation.
BLUESIL TCS 7550 A&B can be further additivated with pigments and fillers, please contact Bluestar Silicones' technical support for more information.
Adhesion to substrate will depend upon the curing conditions. A preliminary test is recommended to determine optimum cure conditions, and a temperature ramp-up in industrial ovens is always preferred to avoid bubbles and ensure best adhesion.
Curing inhibition may occur in contact with certain materials containing tin salts, amines or sulphur. A preliminary test is always recommended.
After use, packaging must be tightly closed and protected against moisture contamination to preserve its properties. When packaging has been opened, material should be used rapidly.
|BLUESIL TCS 7550B may be stored at a temperature between -20 °C/ -4 °F and 30 °C/ 86 °F for up to 12 months from its date of manufacturing.||Please consult the Safety Data Sheet of this product.||ELV;RoHS;WEEE|
BLUESIL TCS 7550B
BLUESIL TCS 7550 A&B is a two-component heat curing liquid silicone elastomer which cures by a polyaddition reaction. All products from the Textile Coating System product line are specially engineered for textile coating applications
Adhesion;Coating;Fabric Coating;Fire Protection;High Temperature Protection;Hydrophobing;Protection;UV resistant;Water Repellency
2 Part RTV
Liquid Silicone Rubber
High bond strength without primer on coated and uncoated fabrics.
Provides high tear strength and edge comb resistance to the coated fabric.
Low thermal conductivity (high insulation properties).
Fast cure at elevated temperature.
Long bath life at room temperature (> 16 h).
Industrial and high performance textile coatings for example thermal insulation and bonding.