It is advised to remix both base and catalyst before mixing them together.
1. Mixing of the two components
To 100 parts of BLUESIL RTV 3322 add 5 parts of Catalyst 24H or 6H.
The two components are thoroughly mixed either using an electrical or pneumatic mixer on a low speed setting so as to limit the inclusion of air in the mixture as well as temperature rise.
After mixing base and catalyst, it is recommended to degas to eliminate entrapped air.
If the processing is done with the help of a machine both parts are degassed before mixing.
The BLUESIL RTV 3322 is degassed under vacuum pressure of 30 to 50 mbar.
Under vacuum pressure, the product will expand 3 at 4 times its initial volume and forms bubble on its surface.
These bubbles will disappear gradually and the mixture will sink back down to its initial volume within 5 to 10 minutes. Release the vacuum and repeat the operation a few minutes later.
Remark: release the vacuum several times improves the degassing. For easier degassing only fill a recipient to 1/3 of its height.
3. Cross linking
The best curing conditions are at 23 °C and 50 % relative humidity. The use of products at higher temperatures and/or relative humidity levels will reduce the pot life and increase the setting rate. As opposed to this, lower temperatures and relative humidity levels will increase the pot life and decrease the setting time. It is recommended not to use the product at temperatures below 20 °C; under these conditions, the final product performance levels will be difficult to achieve.
At 23 °C and 50 % relative humidity, the membranes can be de-moulded after 16 to 24 hours. In order to achieve the best possible performance levels from the membranes, it is preferable to wait for 24 hours before using them. The definitive properties will be acquired after 3 days.
|STORAGE t < +40°C IN ITS ORIGINAL PACK||No special storage precautions noted. Material is stable under normal conditions. Avoid contact with oxidizing agents. Suitable containers: polyethylene. Plastic lined steel drum.||Please consult the Safety Data Sheet of this product.|
BLUESIL RTV 3322
BLUESIL RTV 3322 is a silicone elastomer which, after the addition of catalysts BLUESIL 24H or BLUESIL 6H, cures at room temperature and leads to a flexible and elastic material.
2 Part RTV
- Good fluidity.
- Very good mechanical properties, in particular tear strength.
- Very good flexibility and its low modulus facilitate mould release.
- Odourless catalysts.
Moulds for the production of parts made of different materials, such as plaster, wax, acrylic resin, polyester resin, epoxy resin, as well as silicone elastomers, with following application examples:
- Decoration items: cornices, , ornaments, statues,
- Figurines: toys, candles, statues, giftware,
- Furnishing: furniture and decorative parts,
- Construction: decorative items, pavement, paving stone, columns,
- Artistic foundries: molds for the lost wax casting technique.