Product

 

 

Surface preparation:
All surfaces must be clean and dry, and free from any dust or any traces of contaminants which may affect adhesion.

To degrease, wipe with a pad soaked in solvent then with a clean cloth. Dust should be removed using oil-free compressed air.

- Glass and all glazing materials: degrease with alcohol or methylethyl ketone.

- Aluminium, light alloys, stainless steel: same procedure.

- Other metals: lightly abrade the surface then degrease.

- Wood, lightly abrade the surface then remove dust.

- Plastics : degrease using an agent recommended by the supplier.

- Concrete and other alkaline surfaces: brush and dust.


BLUESIL SLT NOVART does not require a primer on most common substrates, except in the case of immersion, mainly with porous substrates. Please consult us for more information.

In order to improve adhesion on PMMA (sanitary acrylic material), primer BLUESIL PRIM PM820 can be used.


Joint dimensions:
They must take into account the joint movement in addition to local regulations. In order to allow the sealant to operate under the best possible conditions, the minimum cross-section of the seal should be 5 x 5 mm: for seals wider than 12 mm, the thickness will generally be determined as being half this width.


Applying the sealant:
Once a seal back-up material has been put in place (closed-cell polyethylene foam with surface skin or open cell polyurethane foam), the sealant should be applied ensuring that the seal is completely filled. Tool the seal to ensure good contact between the sealant and the bonding surfaces. This should be carried out using a spatula before the surface skin is formed.
Areas soiled with fresh sealant may be cleaned with a dry pad or a pad soaked in a solvent (compatible with the substrate). Any cured sealant can be removed by scraping (e.g. using a razor blade), or by using a special silicone remover product like BLUESIL SILICONE REMOVER.

BLUESIL SLT NOVART TRANSLUCENT may be stored at temperatures between -20°C / -4°F and 30°C / 86°F for up to 12 months from its date of manufacturing.Please consult the Safety Data Sheet of this product.RoHS;VOC

BLUESIL SLT NOVART TRANSLUCENT

BLUESIL SLT NOVART is a one component, neutral  (alcoxy) and fast curing, ready-to-use silicone elastomer suitable for weather-sealing and bonding seals in construction applications. It crosslinks at room temperature to give a flexible seal of low modulus.


BLUESIL SLT NOVART is available in the following colors:

- Translucent

- White

Adhesion;Sealant;Sealing

1 Part RTV Alcoxy

Paste

RoHS;VOC

BLUESIL SLT NOVART combines the advantages of primerless adhesion and neutrality and can be used on numerous substrates such as: glass, layered glass, coated glass, anodised and heat lacquered aluminium, steel, stainless steel, rigid PVC, concrete and other porous substrates.


BLUESIL SLT NOVART does not generally cause staining of surfaces. Nevertheless, specific testing is required in the instance of sensitive surfaces, especially porous ones (marble, stone, etc.).


BLUESIL SLT NOVART can withstand movement of 25% in constant service throughout a wide temperature range.


Once cured, BLUESIL SLT NOVART offers good resistance to concentrated weak acids as well as diluted strong acids and alkali. It also shows good resistance to oxidative agents like bleach, and to alcohols. Good resistance to most common cleaning products is thus anticipated. However, hydrocarbons induce swelling of the sealant. Therefore, contact with hydrocarbons, even short term, should be prohibited.


Once cured, BLUESIL SLT NOVART is highly resistant and is not affected by exposure to sunlight, rain, snow and ozone and maintains this resistance over many years.

BLUESIL SLT NOVART is suitable for weather-sealing and bonding seals for construction and glazing applications such as:

  • Perimeter sealing of wooden, aluminium and PVCu window and door frames.
  • Glazing applications.
  • Expansion joints for facade panels, Curtain wall joint.
  • Ventilation ducts and piping passages.
  • Boat, caravan and camping-car maintenance. 
  • Bonding of roof tiles.

Asia Pacific;Europe Middle East Africa;Central and South America;North America

 Characteristics_A

 

 

Hardness20MonocompISO 868sh.A
Elongation480MonocompNF ISO 37%
Modulus0.3MonocompNF ISO 37MPa
Tensile strength1.1MonocompNF ISO 37MPa

 Characteristics_B

 

 

 

 

 Table_Characteristics_A_And_B

 

 

 

 

 

 

 

 

 

 

 NeedAnExpert

 

 

 

 

 CS

 

 

 SS

 

 

 Certif

 

 

 

 

 Brochures

 

 

 TDS